3A-IGU Insulating Glass Molecular Sieve

3A-IGU insulating glass molecular sieve is silica aluminates in potassium and sodium form with a pore opening of 3 angstroms or 0.3 nm.

Since it continuously and deeply adsorb the residual water and organic volatile in the interlayer of insulating glass, 3A-IGU insulating glass molecular sieve can effectively prevent condensation frosting phenomenon and remain smooth and transparent at very low temperature. Meanwhile, it can fully reduce the large internal and external pressure difference of insulating glass endured from the changes of seasons and diurnal temperature. Also, it has thoroughly solved the distorted broken problem of insulating glass resulted from expansion and contraction. In addition, our product can completely prolong the service life of insulating glass.

Parameter
Technical Specification Units 0,3~0,5mm 0,5~0,9mm 0,8~1,4mm 1,0~1,6mm 1,5~2,0mm 1,2~1,8mm 2,0~2,5mm
Bulk Density g/ml 0.75+/-0.02 0.75+/-0.02 0.73+/-0.02 0.73+/-0.02 0.73+/-0.02 0.73+/-0.02 0.73+/-0.02
Screen Analysis %/min 98 98 98 98 98 98 98
Crush Strength N/min -- 7 10 15 18 20 23
Dust Level Ppm/max 16 25 25 25 25 25 25
Attrition Rate %/max 0.1 0.1 0.1 0.1 0.1 0.1 0.1
Equilibrium H2O Capacity** %/min 16.5 16.5 16.5 16.5 16.5 16.5 16.5
Delta T(25g-25cc) ℃/min 40 40 40 40 40 40 40
N2-adsorbing mg/g max 20 20 20 20 20 20 20
Water Content %/max 1.5 1.5 1.5 1.5 1.5 1.5 1.5

Typical Packaging
3A-IGU insulating glass molecular sieve can be packed in paper box of 25 Kg lined with aluminum foil bag.

As an experienced 3A-IGU insulating glass molecular sieve manufacturer and supplier in China, our company also offers 3A-ETH ethanol dehydration molecular sieve, 3A molecular sieve, fluoride removing activated alumina, and more.

Other Products
    1. 5A-H2 Hydrogen Generation Molecular Sieve Adsorbent5A-H2 hydrogen generation molecular sieve adsorbent is calcium sodium aluminosilicate and its crystal pore diameter is 5 angstroms or 0.5 nm. It is mainly used for pressure swing adsorption equipment to produce hydrogen and carbon monoxide, as well as for the equipment to separate normal alkane ...
    1. 5A-O2 Molecular Sieve for Oxygen Concentrator5A-O2 molecular sieve for oxygen concentrator can provide better effect in specific areas, applied to pressure swing adsorption for air separation to nitrogen and oxygen, as well as preparation of oxygen and oxygen enriched air, and small devices for preparation of oxygen in medical use.